Nitronic 60 Round Bar

  • Home
  • Nitronic 60 Round Bar
Nitronic 60 Round Bar
Nitronic 60 Rod
Nitronic 60 Hex Bar
Nitronic 60 Rounds
Nitronic 60 Round Bar
Nitronic 60 Rod
Nitronic 60 Hex Bar
Nitronic 60 Rounds
Nitronic 60 Round Bar Overview
  • Standard: ASTM A193, A194, A276, A479
  • Round Bar Dia. : 3-600mm
  • Hex Bar Size: 3-180mm
  • Supply State: PH, H&T, ANN
  • Edges: Slit, Square, Round, and V Edge
  • Origin: Indian, European, Japanese
  • Services: Shearing, Cutting, Heat Treatment
  • Tolerances: H13, H10, K10, H12, K9, K11, K12, H8, H9
  • Method: Forged and Rolled
  • MTC: EN 10204 3.1 and 3.2
  • Custom: Yes
  • Delivery: Thailand : 7 Days | Indonesia : 9 Days

Cold and Hot Rolled ASTM A193 UNS S21800 Hex Bar Manufacturer in India With OD 10 to 1000mm

ASTM A193 UNS S21800 Hex Bar Sizes
Standard Specification Size Size Range of Round bars Grades Length Conditions Finishing Finish
ASTM A276, A479 / ASME SA276, SA479 ASTM, ASME and API 6mm to 300 mm 1/2-12" Diameter. Nitronic 60, ALLOY 218, UNS S21800 1 to 6 Meters, Custom Cut Lengths Centreless Ground & Polished, Cold Drawn & Polished Cold Drawn, Polish, Bright & Black Polished & Forged., Black, Turned, Bright, Cold Drawn, Peeled,

 

Nitronic 60 Round Bar

Nitronic 60 Round Bar

AMS 5848 Rod

AMS 5848 Rod

N-60 Stainless Hex Bar

N-60 Stainless Hex Bar

Table Of Content
Nitronic 60 Round Bar Standards
  • UNS: S21800
  • WNR: 1.3964
  • Specification: MS 5848, ASME SB479, ASTM A193, ASTM A194, ASTM A276, ASTM A479
  • International Specification: HPA 50, Alloy 218, N60 Stainless, NAS60
Nitronic 60 Round Bar Standards
Nitronic 60 Round Bar Specification
Round Bar Sizes

Nitronic Alloy 60 Round Bar Sizes

  • Diameter: 3 - 600 mm
  • Length: 0.5 - 6.0 meter
  • Custom Available
Hex Bar Sizes

AMS 5848 Hex Bar Sizes

  • Inscribed Diameter: 3 - 180 mm
  • Length:0.5 - 6.0 meter
  • Custom Available
Physical Properties

Nitronic 60 Round Bar Physical Properties

  • Melting Point:1375°C (2500°F)
  • Density:7.62 g/cc
  • Temprature Range:1800°F (982°C)
Testing

AMS 5848 Hollow Bar Testing

  • PMI
  • Upset Testing
  • Step-Down Tests

Finish

HPA 50 Rounds Finish

  • Rough Turned
  • Polished
  • NO.4, Bright
  • Black
  • Pickled

Origin

N-60 Stainless Threaded Bar Origin

  • American
  • Japanese
  • Indian
  • Korean
  • European
Documentation

Nitronic Alloy 60 Forged Bar Documentation

  • Third Party Inspection Report
  • 100% Radiography Test Report
  • MTC EN 10204 3.1
Shape

Alloy 218 Bright Bar Shape

  • Round
  • Square, Hex
  • Rectangle

Packaging

ASTM A193 UNS S21800 Hex Bar Packaging

  • Bubble wraps
  • Wooden Boxes
  • Custom
Supply Condition

AWS 166 Cold Rolled Round Bar Supply Condition

  • ANN
  • H&T
  • PH
Tolerances

Nitronic® 60 Rod Tolerances

  • K9 to K12
  • H8 to H13

 

Marking

Nitronic Alloy 60 Forged Bar Marking

  • Nominal Size
  • Material Grade
  • Method of Manufacturing etc.
Services

Nitronic 60 Round Bar Services

  • Shearing
  • Heat Treatment
  • Cutting

Method

Nitronic 60 Stainless Steel Rectangular Bar Method

  • Rolled
  • Forged

 

Specialize in Offering Premium AMS 5848 Rod Stock Online With Thickness 700mm or Custom

AMS 5848 Round Bar Size Chart
Size in mm Average Weight
KG/FT KG/MTR
10 0.18 0.62
12 0.30 0.90
14 0.40 1.20
16 0.50 1.60
92 15.91 52.19
93 16.27 53.39
95 16.95 55.65
100 18.79 61.66
28 1.50 4.80
30 1.69 5.55
32 1.90 6.30
34 2.18 7.14
36 2.44 8.00
40 3.00 9.90
45 3.81 12.49
50 4.70 15.40
18 0.60 2.00
20 0.80 2.50
22 0.90 3.00
24 1.08 3.56
63.5 7.58 24.86
65 7.94 26.05
70 9.20 30.20
73 10.00 32.86
75 10.58 34.72
25 1.20 3.90
56 5.89 19.34
125 29.36 96.34
HSN Code of Nitronic 60 Round Bar
Grade HSN Code
Nitronic 60 Round bar 72222099

Industry-leading Nitronic 60 Round Bar Supplier in India known for consistent quality and robust construction.

Nitronic 60 Bar Dimension Chart
Bar Type Diameter / Width (mm) Diameter / Width (inch) Thickness (inch) Thickness (mm) Standard Length (inch) Standard Length (mm)
Round Bar 6 - 350 0.24" - 13.78" - - 39.37" - 236.22" 1000 - 6000
Hex Bar 6 - 75 0.24" - 2.95" - - 39.37" - 236.22" 1000 - 6000
Rectangular Bar 10 - 200 0.39" - 7.87" 0.12" - 3.94" 3 - 100 39.37" - 236.22" 1000 - 6000
N-60 Stainless Threaded Bar Impact Properties
Conditions Test Temperature, °C (°F) Diameter, mm (in.) Charpy V Notch Impact J (ft-lbs)
Cold Swaged 18%, Hardness RC29 -196 (-320) 23.7 (0.932) 91 (67)
Cold Swaged 40%, Hardness RC37 -196 (-320) 20.2 (0.795) 54 (40)
Cold Swaged 54%, Hardness RC42 -196 (-320) 17.8 (0.700) 35 (26)
Cold Swaged 18%, Hardness RC29 -129 (-200) 23.7 (0.932) 122 (90)
Cold Swaged 40%, Hardness RC37 -129 (-200) 20.2 (0.795) 60 (44)
Cold Swaged 54%, Hardness RC42 -129 (-200) 17.8 (0.700) 41 (30)
Annealed Room Temperature 25.4 (1) 325 (240)*
Annealed -73 (-100) 25.4 (1) 310 (229)
Annealed -196 (-320) 25.4 (1) 195 (144)
Annealed Room Temperature 54.2 (2.25) 325 (240)*
Annealed -73 (-100) 54.2 (2.25) 325 (240)*
Annealed -196 (-320) 54.2 (2.25) 217 (160)

High-end Nitronic 60 Round Bar Supplier in India offering expertly designed products that exceed industry standards.

Machining Data for Alloy 218 Rectangular Bar
Machining Type Suggested Starting Rates
Single Point turning :
  • Roughing - 0.15" depth, 0.015"/rev feed -175 SFM
  • Finishing - 0.025" depth, 0.007"/rev feed - 200 SFM
Side and Slot Milling :
  • Roughing - 0.25" depth - 0.007"/tooth feed - 125SFM
  • Finishing - 0.050" depth - 0.009"/tooth feed - 140SFM
Drilling :
  • 1/4" Dia hole - 0.004"/rev feed - 60 SFM
  • 1/2" Dia hole - 0.007"/rev feed - 60 SFM
  • 3/4" Dia hole - 0.010"/rev feed - 60 SFM
Reaming :
  • Feed - same as drilling - 100 SFM

Trusted Supplier Of Alloy 218 Rectangular Bar in Mumbai Tested With Liquid Penetrant Testing

Alloy 218 Rectangular Bar Testings
Alloy 218 Rectangular Bar Testings

 

AWS 166 Cold Rolled Round Bar Fatigue Strength
Condition Fatigue Limit, MPa (ksi) 10⁸ Cycles Diameter, mm (in.) Hardness
Annealed 258 (37.5) 25.4 (1) 95 HRB
Cold Worked 54.6% 500 (72.5) 17.8 (0.70) 44 HRC
Welding Electrodes for Nitronic 60 Round Bars
Nitronic Grade Special Electrodes Matching El@ctrod@s or Filler Metals (AWS AS .4/S.9) Substitute El@ctrod@s or Filler Metals (AWS AS .4/S.9)
60
  • Sode 336*
  • Sode 3500**
 ER218 -
Magnetic Permeability of N-60 Stainless HS Bar
Bar Location Field Strength Ampere/Metres (Oersteds)
7958 (100) 15 916 (200) 39 790 (500) 79 580 (1,000)
Surface 1.0009 1.0040 1.0029 1.0029
Central 1.0013 1.0024 1.0033 1.0031
Intermediate 1.0003 1.0022 1.0039 1.0029
Nitronic 60 Rod Types
Nitronic 60 Round Bar

Nitronic 60 Round Bar

Nitronic® 60 Rod

Nitronic® 60 Rod

ASTM A193 UNS S21800 Hex Bar

ASTM A193 UNS S21800 Hex Bar

Nitronic 60 Stainless Steel Rectangular Bar

Nitronic 60 Stainless Steel Rectangular Bar

Alloy 218 Bright Bar

Alloy 218 Bright Bar

HPA 50 Rounds

HPA 50 Rounds

AMS 5848 Hollow Bar

AMS 5848 Hollow Bar

N-60 Stainless Threaded Bar

N-60 Stainless Threaded Bar

AWS 166 Cold Rolled Round Bar

AWS 166 Cold Rolled Round Bar

Nitronic Alloy 60 Forged Bar

Nitronic Alloy 60 Forged Bar

Custom Stainless Steel Grade NITRONIC® 60 Annealed Round Bar

Custom Stainless Steel Grade NITRONIC® 60 Annealed Round Bar

Nitronic 60 Polished Bar

Nitronic 60 Polished Bar

 

Established Nitronic 60 Round Bar Supplier in India of reliable goods tailored for harsh industrial applications.

Nitronic 60 Round Bar Double Shear Strength
% Cold Drawn Shear Strength, MPa (ksi)
10 614 (89)
20 676 (98)
30 731 (106)
40 779 (113)
50 841 (122)
60 896 (130)
Carries a Wide Range of Forged HPA 50 Bright Bar With Excellent Galling Resistance At Factory Price
Nitronic® 60 Round Bar Tolerance Chart
Diameters (mm) 13 12 11 10 9 8 7 6
>1 ≤ 3 0.140 0.090 0.060 0.040 0.025 0.014 0.009 0.007
>3 ≤ 6 0.180 0.120 0.075 0.048 0.030 0.018 0.012 0.008
>50 ≤ 80 0.460 0.300 0.190 0.120 0.074 0.046 - 0.019
>6 ≤ 10 0.220 0.150 0.090 0.058 0.036 0.022 0.015 0.009
>10 ≤ 18 0.270 0.180 0.110 0.070 0.043 0.027 0.018 0.011
>18 ≤ 30 0.330 0.210 0.130 0.084 0.052 0.033 0.021 0.013
>30 ≤ 50 0.390 0.250 0.160 0.100 0.062 0.039 0.025 0.016
>315 ≤ 400 0.890 0.570 0.360 - - - - -
>80 ≤ 120 0.540 0.350 0.220 0.140 0.087 - - 0.022
>120 ≤ 180 0.630 0.400 0.250 0.160 0.100 - - 0.025
>180 ≤ 250 0.720 0.460 0.290 0.185 0.115 - - -
>250 ≤ 315 0.810 0.520 0.320 - - - - -
>400 ≤ 500 0.970 0.630 0.400 - - - - -
>500 1.100 0.700 0.440 - - - - -
Recommended Machining Rates for Nitronic 60 Rod
Machining Operation Cutting Rates, Depth/Rev Feed Cutting Rates, SFM
Drilling
0.50 in. diameter hole 0.007 60
0.75 in. diameter hole 0.010 60
0.25 in. diameter hole 0.004 60
Single Point Turning Carbide Tools
Finishing 0.025 - 0.007 203 394
Roughing 0.150 - 0.015 197 328
Side and Slot Milling
Finishing 0.050 0.009 140
Roughing 0.250 0.007 125
Reaming*
0.50 in. diameter hole 0.007 100
0.75 in. diameter hole 0.010 100
0.25 in. diameter hole 0.004 100
Typical Elevated Temperature Properties of N-60 Stainless Billet
Test Temperature, °C (°F) UTS, MPa (ksi) 0.2% YS, MPa (ksi) Elongation % in 4Do Reduction of Area %
24 (75) 662 (96) 324 (47) 54 55
93 (200) 586 (85) 255 (37) 61 61
204 (400) 496 (72) 193 (28) 62 64
316 (600) 462 (67) 165 (24) 60 60
427 (800) 434 (63) 159 (23) 58 64
538 (1000) 421 (61) 159 (23) 57 64
649 (1200) 379 (55) 159 (23) 50 57

Leading Nitronic 60 Round Bar Stockist in India offering precision and durability in every product delivered.

AMS 5848 Rod Stress Rupture Strength
Test Temperature, °C (°F) Stress, MPa (ksi) Reduction of Area % Elongation % in 4Do Time to Failure Hours
649 (1200) 207 (30) 48 29 108
649 (1200) 241 (35) 31 23 34
649 (1200) 172 (25) 53 32 348
HPA 50 Bright Bar Chemical Composition

Cr 16.00%

Ni 8.00%

Si 3.50 %

Mn 7.00%

N 0.08%

Alloy 218 Rectangular Bar Torsion And Shear Properties
Condition Diameter 0.2% Torsional YS, MPa (ksi) Hardness Double Shear Strength Torsional Modulus G, Modulus of Rupture
mm, (in.) γ ε HRB MPa (ksi) GPa (Mpsi) MPa (ksi)
Annealed 25.4 (1) 337 (48.9) 350 (50.7) 95 - 61 (8.83) 855 (124)
Annealed 9.5 (0.375) - - 95 593 (86) - -
Thermal Properties of Nitronic Alloy 60 Round Bar
Thermal Properties Metric English
CTE, linear     
  • 15.8 µm/m-°C
  • Temperature 25.6 - 93.3 °C
  • 8.80 µin/in-°F
  • Temperature 78.0 - 200 °F
  • 17.3 µm/m-°C
  • Temperature 25.6 - 316 °C
  • 9.60 µin/in-°F
  • Temperature 78.0 - 600 °F
  • 18.5 µm/m-°C
  • Temperature 25.6 - 649 °C
  • 10.3 µin/in-°F
  • Temperature 78.0 - 1200 °F
  • 19.8 µm/m-°C
  • Temperature 25.6 - 982 °C
  • 11.0 µin/in-°F
  • Temperature 78.0 - 1800 °F

Preferred Nitronic 60 Round Bar Stockist in India for industries requiring strength, resilience, and precision.

HPA 50 Bright Bar Wear and Calling Properties
Grade Hardness Weight Loss
Rockwell Mg / 1000 cycles
105 rpm 415 rpm
Nitronic 60 B95 2.79 1.58
Electrical Properties of Alloy 218 Rectangular Bar
Electrical Properties Metric English
Electrical Resistivity  0.0000982 ohm-cm 0.0000982 ohm-cm
Typical Bearing Properties of Alloy 218 Bright Bar
Condition Bearing Strength, MPa (ksi) 0.2% YS, MPa (ksi) Bearing yield Strength, MPa (ksi) Elongation % in 4D0 UTS, MPa (ksi) Hardness, (R)
Annealed 25.4 (1) 64 414 (60) 95 HRB 710 (103) 74
Finds Extensive Stock Of N-60 Stainless Threaded and Hollow Bar For High-temperature Applications
N-60 Stainless Threaded Bar Applications
N-60 Stainless Threaded Bar Applications

 

Physical Properties of Nitronic® 60 Round Bar
Properties Metric US
Density 7.62 g/cc 0.275 lb/in³
Modulus of Elasticity 181 GPa 26200 ksi
Bend Radius, Minimum 1.5 t 1.5 t
Reduction of Area 21.5 % 21.5 %

Trusted Nitronic 60 Round Bar Manufacturer in India delivering materials with superior resistance and reliability

Nitronic 60 Hot-Rolled Round Bars Mechanical Properties
Grade Yield Strength 0.2% Proof (ksi) min Tensile Strength (ksi) min Elongation (% in 50mm) min Hardness
Nitronic 60 55 105 35 -
Nitronic 60 Round Bar Equivalent
North America
UNS
(North America)

S21800

German
DIN
(German)

1.3964

High Temperature Wear Resistance Of Nitronic 60* Bar
Alloy Atmosphere Wear Index Volume Loss, mm³
NITRONIC 60 Helium 38.3 6.94
Air + Steam 30.4 8.74
Air + Steam 25.2 10.57
Alloy 218 Bright Bar Carburization Resistance
Alloy Condition 0.2% YS, MPa (ksi) UTS, MPa (ksi) Reduction of Area Bend 1.5T Elongation % in 4D0
NITRONIC 60 Unexposed 341 (49.5) 800 (116.0) 66 180° 74
Exposed 400 (58.0) 630 (91.5) 22 100° 19
Sulfide Stress Cracking Of Nitronic 60 Bars
% Yield Strength Applied Stress MPa (ksi) Time to Failure Hours Location
100 669 (97)
  • 235
  • 160
  • 132
  • Surface
  • Intermediate
  • Central
75 503 (73)
  • 302
  • 208
  • 227
  • Surface
  • Intermediate
  • Central
60 400 (58)
  • 720 NF#
  • 720 NF
  • 720 NF
  • Surface
  • Intermediate
  • Central
50 338 (49)
  • 720 NF
  • 720 NF
  • 720 NF
  • Surface
  • Intermediate
  • Central
HPA 50 Bright Bar Magnetic Permeability
Condition Magnetic Permeability (μ)
Annealed 1.003
25% Cold Drawn 1.004
50% Cold Drawn 1.007
75% Cold Drawn 1.010
Nitronic 60 Round Bar Delivery Time As Per Location
Category Countries Delivery Time
Fast Delivery (Under 10 Days) Japan Japan 5 Days
Qatar Qatar 7 Days
Sri lanka Sri lanka 8 Days
Medium Delivery (25–30 Days) Sudan Sudan 30 Days
Long Delivery (40+ Days) Mexico Mexico 25–30 Days
Gabon Gabon 30 Days
Panama Panama 30 Days
Round Bar in Stock
Make a Call for Any Type Query.
+(91)-(22)-6777 6777
Frequently Asked Questions

Nitronic 60 Stainless Steel Rectangular Bar is supplied in PH, H&T, ANN condition, or as specified.

There is no fixed MOQ for Alloy 218 Bright Bar; we supply any quantity.

Yes, we supply HPA 50 Rounds in custom sizes, thickness and length as required.

AMS 5848 Hollow Bar is manufactured per ASTM A193 and supplied with MTC on request.

N-60 Stainless Threaded Bar ships ex-stock quickly; custom orders dispatch within two to five weeks.