Nitronic 50 Flat Rod
Nitronic® 50 Bright Flat Bar
UNS S20910 Cold Drawn Flat Bar
Nitronic 50 Flat Bar Sizes
Nitronic 50 Flat Rod Sizes
AMS 5764 Rolling Flat Bar Physical Properties
AMS 5764 Rolling Flat Bar Testing
FXM-19 Hot Rolled Flat Bar Finish
WNR 1.3964 Flat Angle Bar Origin
UNS S20910 Cold Drawn Flat Bar Documentation
Nitronic® 50 Bright Flat Bar Shape
Nitronic 50 Flat Rod Packaging
Nitronic® 50 Bright Flat Bar Supply Condition
FXM-19 Hot Rolled Flat Bar Tolerances
AMS 5764 Rolling Flat Bar Marking
FXM-19 Hot Rolled Flat Bar Services
UNS S20910 Cold Drawn Flat Bar Method
Renowned Nitronic 50 Flat Bar Supplier in India of top-grade materials, crafted for longevity and reliability.
| Condition | Size, mm (in.) | 0.2% YS, MPa (ksi) | UTS, MPa (ksi) | Rockwell Hardness Max. | Reduction of Area, % | Elongation % in 4D₀ | Impact Strength -60°C (-76°F), J (ft-lbs) | Impact Strength & Lateral Expansion -196°C (-321°F) J (ft-lbs) / mm (in.) |
Lateral Expansion -60°C (-76°F), mm (in.) |
|---|---|---|---|---|---|---|---|---|---|
| Annealed | all | 415 (60) | 690 (100) | C35 | 55 | 35 | 20 (15) | 27 (20) 0.381 (0.015) |
0.381 (0.015) |
| HS | 0–50.8 (0–2) | 800 (116) | 930 (135) | C35 | 50 | 20 | 20 (15) | 27 (20) 0.381 (0.015) |
0.381 (0.015) |
| HS | > 50.8–76.2 (> 2–3) | 515 (75) | 800 (116) | C35 | 50 | 25 | 20 (15) | 27 (20) 0.381 (0.015) |
0.381 (0.015) |
| HS | > 76.2–203.2 (> 3–8) | 415 (60) | 700 (102) | C35 | 50 | 30 | 20 (15) | 27 (20) 0.381 (0.015) |
0.381 (0.015) |
| SHS | 0–50.8 (0–2) | 800 (116) | 930 (135) | C35 | 50 | 20 | 20 (15) | 27 (20) | 0.381 (0.015) |
| SHS | > 50.8–145 (> 2–5.7) | 725 (105) | 900 (131) | C35 | 50 | 25 | 20 (15) | 27 (20) 0.381 (0.015) |
0.381 (0.015) |
| Test Temperature °C (°F) |
Impact – Charpy V. Notch, J (ft-lbs) | |
|---|---|---|
| Annealed at 1121 °C (2050 °F) | Simulated HAZ | |
| 24 (75) | 230 (170) | 230 (170) |
| -73 (-100) | 156 (115) | 156 (115) |
| -196 (-320) | 68 (50) | 68 (50) |
Industry-leading Nitronic 50 Flat Bar Supplier in India known for consistent quality and robust construction.
Reliable Nitronic 50 Flat Bar Manufacturer in India with a reputation for precision, quality, and endurance.
| Condition | Bar Diameter, mm (in.) |
Fatigue Strength at 10⁸ Reversals of Stress, MPa (ksi) | |
|---|---|---|---|
| Tested in Air* | Tested in Seawater** | ||
| High-Strength (HS) Bars (Hot Rolled Unannealed) | 25.4 (1) | 469 (68) | 124 (18) |
| 63.5 (2.5) | 400 (58) | 103 (15) | |
| 102 (4) | 303 (44) | 103 (15) | |
| Annealed 1121 °C (2050 °F) |
25.4 (1) | 290 (42) | 152 (22) |
| Annealed 1066 °C (1950 °F) |
25.4 (1) | 324 (47) | – |
Established Nitronic 50 Flat Bar Supplier in India of reliable goods tailored for harsh industrial applications.
| - | 0.2% YS, MPa (ksi) | Prop. Limit, MPa (ksi) |
Modulus of Rupture, MPa (ksi) |
|---|---|---|---|
| Typical | 690 (100) | 448 (65) | 965 (140) |
| Minimum | 483 (70) | 345 (50) | 827 (120) |
| Property | Value |
|---|---|
| Density | 8.03 g/cm³ |
| Modulus of Elasticity | 190 GPa |
| Thermal Conductivity | 14.6 W/m·K |
| Specific Heat | 500 J/kg·K |
| Melting Point | 1390-1425 °C |
| Condition | Test Temperature °C (°F) |
Stress for Min Creep Rate, MPa (ksi) 0.00001% per Hour | Stress for Min Creep Rate, MPa (ksi) 0.0001% per Hour |
|---|---|---|---|
| Annealed 1121 °C (2050 °F) |
593 (1100) | 238 (34.5) | 283 (41) |
| 649 (1200) | 110 (16) | 152 (22) |
Certified Nitronic 50 Flat Bar Stockist in India of high-integrity products with proven resistance to fatigue.
| Condition | Test Temperature, °C (°F) | Stress for Failure, MPa (ksi) | ||
|---|---|---|---|---|
| 100 Hours | 1,000 Hours | 10,000 Hours (estimated) | ||
| Annealed 1121 °C (2050 °F) Bars 25.4 - 38.1 mm (1 - 1.5 in.) Diameter |
538 (1000) | - | - | - |
| 593 (1100) | 488 (65) | 372 (54) | 296 (43) | |
| 649 (1200) | 345 (50) | 283 (41) | 224 (32.5) | |
| 732 (1350) | 200 (29) | 103 (15) | 58.6 (8.5) | |
| 816 (1500) | 89.6 (13) | 44.8 (6.5) | 24.1 (3.5) | |
| Annealed 1066 °C (1950 °F) Bars 19.1 - 31.8 mm (0.75 - 1.25 in.) Diameter |
538 (1000) | 627 (91) | 607 (88) | 496 (72) |
| 593 (1100) | 496 (72) | 427 (62) | 324 (47) | |
| 649 (1200) | 379 (55) | 262 (38) | 152 (22) | |
| 732 (1350) | 145 (11) | 82.7 (12) | 41.4 (6) | |
| 816 (1500) | 69.0 (10) | 25.5 (3.7) | 9.0 (1.3) | |
| Condition as supplied by AWI | Temperature | Type | Time | Cooling |
|---|---|---|---|---|
| Annealed or Spring Temper | 250 °C (480 °F) | Stress Relieve | 1 Hr | Air |
Leading Nitronic 50 Flat Bar Stockist in India offering precision and durability in every product delivered.
| Temperature, °C (°F) | Thermal Conductivity*, W/m/K (BTU/hr/ft/in./°F) |
|---|---|
| 21 (70) | - |
| 149 (300) | 15.6 (108) |
| 316 (600) | 17.9 (124) |
| 482 (900) | 20.3 (141) |
| 649 (1200) | 23.0 (160) |
| 816 (1500) | 25.2 (175) |
| Condition | UTS,MPa (ksi) | Shear/Tensile Ratio, % | Double Shear,MPa (ksi) |
|---|---|---|---|
| Annealed 1066 °C (1950 °F) | 869 (126) | 69 | 598 (86.8) |
| Annealed 1121 °C (2050 °F) | 779 (113) | 69.5 | 541 (78.5) |
Reliable Nitronic 50 Flat Bar Stockist in India with a commitment to innovation and product integrity.
| Condition | Test Temperature, °C (°F) | 0.2% YS, MPa (ksi) | UTS, MPa (ksi) | Reduction of Area, % | Elongation % in 4D₀ |
|---|---|---|---|---|---|
| Annealed 1066 °C (1950 °F) Bars 19.1 – 31.8 mm (0.75 – 1.25 in.) Diameter |
24 (75) | 538 (78) | 855 (124) | 68 | 41 |
| 93 (200) | 455 (66) | 772 (112) | 68 | 41 | |
| 204 (400) | 400 (58) | 703 (102) | 67 | 38 | |
| 316 (600) | 372 (54) | 676 (98) | 64 | 38 | |
| 427 (800) | 345 (50) | 648 (94) | 63 | 40 | |
| 538 (1000) | 303 (44) | 552 (80) | 63 | 37 | |
| 732 (1350) | 290 (42) | 469 (68) | 72 | 43 | |
| 816 (1500) | 221 (32) | 345 (50) | 85 | 40 | |
| Annealed 1121 °C (2050 °F) Bars 25.4 – 38.1 mm (1 – 1.5 in.) Diameter |
24 (75) | 414 (60) | 807 (117) | 71 | 45 |
| 93 (200) | 332 (48) | 738 (107) | 71 | 41 | |
| 204 (400) | 262 (38) | 662 (96) | 70 | 40 | |
| 316 (600) | 241 (35) | 634 (92) | 68 | 43 | |
| 427 (800) | 234 (34) | 610 (89) | 66 | 44 | |
| 538 (1000) | 214 (31) | 510 (74) | 64 | 38 | |
| 732 (1350) | 214 (31) | 455 (66) | 62 | 41 | |
| 816 (1500) | 207 (30) | 359 (52) | 61 | 41 |
| Temperature, °C (°F) | Coefficient of Thermal Expansion (µin./in./°F) | Coefficient of Thermal Expansion (µm/m/K) |
|---|---|---|
| 21 – 93 (70 – 200) | 9.0 | 16.2 |
| 21 – 204 (70 – 400) | 9.2 | 16.6 |
| 21 – 316 (70 – 600) | 9.6 | 17.3 |
| 21 – 427 (70 – 800) | 9.9 | 17.8 |
| 21 – 538 (70 – 1000) | 10.2 | 18.4 |
| 21 – 649 (70 – 1200) | 10.5 | 18.9 |
| 21 – 760 (70 – 1400) | 19.4 | 10.8 |
| 21 – 871 (70 – 1600) | 11.1 | 20.0 |
| Temperature, °C (°F) | Contraction Parts Per Million (ppm) | Mean Expansion Coefficient Between T and 24 °C (75 °F) — ppm/°F | Mean Expansion Coefficient Between T and 24 °C (75 °F) - ppm/°C |
|---|---|---|---|
| -41 (-41) | 948 | 8.17 | 14.61 |
| -46 (-51) | 1016 | 8.06 | 14.53 |
| -51 (-60) | 1074 | 7.95 | 14.34 |
| -62 (-80) | 1237 | 7.98 | 14.40 |
| -73 (-100) | 1398 | 7.99 | 14.43 |
| -87 (-125) | 1560 | 7.80 | 14.07 |
| -101 (-150) | 1723 | 7.66 | 13.80 |
| -117 (-178) | 1951 | 7.47 | 13.84 |
| -129 (-200) | 2079 | 7.56 | 13.60 |
| -143 (-225) | 2231 | 7.44 | 13.37 |
| -162 (-260) | 2333 | 6.96 | 12.55 |
| -196 (-320) | 2542 | 6.44 | 11.56 |
| Temperature, °C (°F) | Young’s Modulus in Tension | Poisson’s Ratio | |
|---|---|---|---|
| GPa | Mpsi | ||
| 22 (72) | 199 | 28.9 | 0.312 |
| 93 (200) | 192 | 27.8 | 0.307 |
| 149 (300) | 186 | 27.0 | 0.303 |
| 204 (400) | 180 | 26.1 | 0.299 |
| 260 (500) | 174 | 25.3 | 0.295 |
| 315 (600) | 170 | 24.6 | 0.291 |
| 371 (700) | 165 | 24.0 | 0.288 |
| Condition | UTS – Smooth, MPa (ksi) | UTS – Notched, MPa (ksi) |
|---|---|---|
| Annealed 1121 °C(2050 °F) | 790 (114.5) | 1069 (155) |
| Annealed 1066 °C(1950 °F) | 830 (120.5) | – |
| High-Strength (HS) bars | 1041 (151.0) | 1355 (196.5) |
| Condition | Typical Magnetic Permeability at Field Strength of | ||
|---|---|---|---|
| 50 Oer (3978 A/m) | 100 Oer (7957 A/m) | 200 Oer (15 914 A/m) | |
| Annealed | 1.004 | 1.004 | 1.004 |
| Cold Drawn 27% | 1.004 | 1.004 | 1.003 |
| Cold Drawn 56% | 1.004 | 1.004 | 1.004 |
| Cold Drawn 75% | 1.004 | 1.004 | 1.004 |
| Temperature, °C (°F) | Magnetic Mass Susceptibility, χ, 10⁶ cm³/g | Typical Magnetic Permeability, μ |
|---|---|---|
| 22 (72) | 21.5 | 1.0021 |
| -23 (-9) | 22.5 | 1.0022 |
| -73 (-99) | 25.0 | 1.0025 |
| -123 (-189) | 28.5 | 1.0028 |
| -173 (-279) | 35.5 | 1.0035 |
| -223 (-369) | 54.0 | 1.0053 |
| -240 (-400) | 74.0 | 1.0073 |
| -258 (-432) | 61.0 | 1.0060 |
| Category | Countries | Delivery Time | |
|---|---|---|---|
| Fast Delivery (Under 10 Days) | UAE |  |
5 Days |
| Qatar |  |
7 Days | |
| Singapore |  |
8 Days | |
| Medium Delivery (25–30 Days) | South Africa |  |
25–30 Days |
| Italy |  |
30 Days | |
| France |  |
30 Days | |
| Long Delivery (40+ Days) | USA |  |
40–60 Days |
UNS S20910 Cold Drawn Flat Bar is carefully export-packed in wooden crates or bundles with moisture-proof wrapping.
Share your required size and quantity for WNR 1.3964 Flat Angle Bar; we quote within 24 hours.
FXM-19 Hot Rolled Flat Bar is available in mill, pickled, polished or bright finish as per your project.
We source AMS 5764 Rolling Flat Bar from Indian, European and Japanese mills, all fully certified.
Nitronic 50 Flat Bar is supplied in PH, H&T, ANN condition, or as specified.