| Diameter (mm) | Diameter (inches) | Estimated Weight (kg/m) |
|---|---|---|
| 10 | 0.394 | 0.62 |
| 12 | 0.472 | 0.89 |
| 16 | 0.630 | 1.58 |
| 20 | 0.787 | 2.47 |
| 25 | 0.984 | 3.85 |
| 32 | 1.260 | 6.31 |
| 40 | 1.575 | 9.85 |
| 50 | 1.969 | 15.40 |
| 65 | 2.559 | 26.00 |
| 75 | 2.953 | 33.00 |
| 100 | 3.937 | 61.60 |
Nitronic 50 Round Bar
UNS S20910 Rod
WNR 1.3964 Hex Bar
N-50 Stainless Round Bar Sizes
Nitronic Alloy 50 Hex Bar Sizes
UNS S20910 Hex Bar Physical Properties
FXM-19 Bright Bar Testing
AMS 5764 Threaded Bar Finish
Forged Alloy 50 Hollow Bar Origin
WNR 1.3964 Rectangular Bar Documentation
Nitronic 50 Round Bar Shape
UNS S20910 Hex Bar Packaging
XM 19 Polished Bar Supply Condition
Aquamet 22 Rounds Tolerances
Aquamet 2 Bright Bar Marking
Nitronic Alloy 50 Annealed Round Bar Services
Alloy 50 Rectangular Bar Method
| Type | SIZES (Inches) | SIZES (mm) | ISO Tolerance |
|---|---|---|---|
| Peeled and Polished | 1.50" – 6.00" | 40.00 – 150.00 | h11, h11-DIN 1013 |
| Cold Drawn and Ground | 5/6" – 2.50" | 10.00 – 75.00 | h8-h9-h10-h11 |
| Cold Drawn and Polish | 1/8" – 3.00" | 3.00 – 75.00 | h8-h9-h10-h11 |
| Peeled and Ground | 3/4″ – 2.00" | 20.00 – 50.00 | h9-h10-h11 |
| Heat Treatment Process | Temperature Range |
|---|---|
| Stress Relieving | 600°C to 700°C |
| Hardening | 950°C to 1050°C |
| Solution Annealing | 1050°C to 1150°C |
| Tempering | 300°C to 500°C |
Dependable Nitronic 50 Round Bar Supplier in India with a focus on performance, safety, and innovation.
| Size (Width x Thickness) | Weight (per foot) | Standard Length |
|---|---|---|
| 1/2″ x 1-1/2″ | 2.52 lbs | 12 ft |
| 3/4″ x 1-1/2″ | 3.78 lbs | 12 ft |
| 3/4″ x 2″ | 5.04 lbs | 12 ft |
| 1″ x 2″ | 6.72 lbs | 12 ft |
| 1″ x 3″ | 10.08 lbs | 12 ft |
| 1/4″ x 1/2″ | 0.56 lbs | 12 ft |
| 1/4″ x 3/4″ | 0.84 lbs | 12 ft |
| 3/8″ x 1/2″ | 0.84 lbs | 12 ft |
| 3/8″ x 3/4″ | 1.26 lbs | 12 ft |
| 1/2″ x 1″ | 1.68 lbs | 12 ft |
| Diameter Range (mm) | Permitted Variation (mm) |
|---|---|
| ≥6 to ≤18 | +0 / -0.070 |
| >30 to ≤50 | +0 / -0.100 |
| >18 to ≤30 | +0 / -0.085 |
| >50 to ≤80 | +0 / -0.120 |
| >80 to ≤100 | +0 / -0.140 |
| Conditions | Practice B Ferric Sulfate, mm/y (MPY) | Practice E Copper-Copper Sulfate |
|---|---|---|
| Annealed 1121 °C (2050 °F) | 0.27 (10.8) | Passed |
| Annealed 1121 °C (2050 °F) + 677 °C (1250 °F) – 1 hr – A.C. | 0.67 (26.4) | Passed |
| Annealed 1066 °C (1950 °F) | 0.30 (12.0) | Passed |
| Annealed 1066 °C (1950 °F) + 677 °C (1250 °F) – 1 hr – A.C. | 1.16 (45.6) | Passed |
| High-Strength (Bar Mill) | 0.94 (37.2) | Passed |
High-Strength (Precision Rotary Forging, PRF):
|
|
|
Industry-leading Nitronic 50 Round Bar Supplier in India known for consistent quality and robust construction.
| Size | Kgs / Foot | Kgs / Mtr | Size | Kgs / Foot | Kgs / Mtr | Size | Kgs / Foot | Kgs / Mtr |
|---|---|---|---|---|---|---|---|---|
| 3 | 0.017 | 0.055 | 20 | 0.753 | 2.470 | 3" | 10.900 | 35.762 |
| 5/32" | 0.029 | 0.095 | 7/8" | 0.926 | 3.038 | 3-1/2" | 14.850 | 48.772 |
| 4 | 0.030 | 0.098 | 24 | 1.080 | 3.543 | 3-3/4" | 17.001 | 55.780 |
| 3/16" | 0.043 | 0.141 | 25 | 1.180 | 3.871 | 4" | 19.306 | 63.340 |
| 5 | 0.047 | 0.154 | 1" | 1.210 | 3.970 | 4-1/4" | 21.908 | 72.249 |
| 7/32" | 0.058 | 0.190 | 26 | 1.271 | 4.170 | 4-1/2" | 24.4487 | 80.340 |
| 8 | 0.120 | 0.398 | 32 | 1.894 | 6.314 | 6-1/2" | 51.093 | 167.630 |
| 9 | 0.152 | 0.498 | 1-3/8" | 2.303 | 7.550 | 7" | 59.432 | 196.000 |
| 3/8" | 0.170 | 0.557 | 35 | 2.390 | 7.553 | 7-1/2" | 68.226 | 225.000 |
| 10 | 0.189 | 0.620 | 36 | 2.438 | 7.999 | 8" | 77.586 | 254.55 |
| 6 | 0.068 | 0.223 | 27 | 1.368 | 4.490 | 4-3/4" | 27.366 | 90.249 |
| 1/4" | 0.076 | 0.249 | 1-1/8" | 1.534 | 5.033 | 5" | 30.461 | 99.940 |
| 7 | 0.091 | 0.298 | 30 | 1.691 | 5.548 | 5-1/2" | 36.690 | 121.000 |
| 5/16" | 0.118 | 0.387 | 1-1/4" | 1.924 | 6.349 | 6" | 43.860 | 143.900 |
| 1/8" | 0.019 | 0.062 | 22 | 0.908 | 2.979 | 3-1/4" | 12.800 | 41.996 |
| 11 | 0.228 | 0.748 | 38 | 2.792 | 8.903 | 10" | 121.048 | 397.140 |
| Alloy | Condition | 0.2% YS, MPa (ksi) | Rockwell Hardness, C | Time to Failure, hr, Under Stress, MPa (ksi) | ||||||
|---|---|---|---|---|---|---|---|---|---|---|
| 1034 (150) | 965 (140) | 862 (125) | 690 (100) | 517 (75) | 345 (50) | 172 (25) | ||||
| NITRONIC 50 | Annealed 1066 °C (1950 °F) | 488 (67) | 22 | - | - | - | > 1000 | > 1000 | > 1000 | - |
| High-Strength (HS)(3) 25.4 mm (1 in.) dia. | 931 (135) | 33 | - | 204 | 320 | > 1000 | > 1000 | - | - | |
| High-Strength (HS)(3) 25.4 mm (1 in.) dia. | 1007 (146) | 35 | - | - | 358 | - | - | - | - | |
| High-Strength (HS)(3) 25.4 mm (1 in.) dia. | 993 (144) | 36 | 170(2) | > 1000 | > 1000 | > 1000 | - | - | - | |
| Cold Drawn 9.5 mm (0.375 in.) dia. | 1103 (160) | 41 | > 1000 | - | - | > 1000 | - | - | - | |
Reliable Nitronic 50 Round Bar Supplier in India with a commitment to innovation and product integrity.
| Condition | Bar Diameter, mm (in.) | Fatigue Strength at 108 Reversals of Stress, MPa (ksi) | |
|---|---|---|---|
| Tested in Seawater** | Tested in Air* | ||
| Annealed 1121 °C (2050 °F) | 25.4 (1) | 152 (22) | 290 (42) |
| Annealed 1066 °C (1950 °F) | 25.4 (1) | - | 324 (47) |
| High-Strength Bars | 25.4 (1) | 103 (15) | 303 (44) |
| 63.5 (2.5) | 124 (18) | 469 (68) | |
| 102 (4) | 103 (15) | 400 (58) | |
| Temperature, °F | -320 | -100 | 75 | 200 | 400 | 600 | 800 | 1000 | 1200 | 1350 | 1500 |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.2% Yield Strength, ksi | - | - | 60 | 50 | 38 | 35 | 34 | 32 | 31 | 31 | 30 |
| Ultimate Tensile Strength, ksi | - | - | 117 | 107 | 96 | 92 | 89 | 84 | 74 | 66 | 52 |
| Elongation, 2% | - | - | 45 | 43.5 | 43.5 | 42.5 | 43.5 | 41 | 38 | 37 | 41 |
| Impact Strength, ft-lbs | 50 | 115 | 170 | - | - | - | - | - | - | - | - |
Quality-first Nitronic 50 Round Bar Stockist in India trusted by leading brands across the globe.
| Machining Operation | Cutting Rates, m/min | Cutting Rates, SFM |
|---|---|---|
| Automatic Screw Machine | 14 - 20 | 45 - 65 |
| Single Point Turning Carbide Tools, Roughing | 60 - 100 | 197 - 328 |
| Single Point Turning Carbide Tools, Finishing | 80 - 120 | 263 - 394 |
| High Cobalt or Cast Alloy Tools, Roughing | 15 - 20 | 50 - 65 |
| High Cobalt or Cast Alloy Tools, Finishing | 15 - 23 | 50 - 75 |
| High-Speed Steel Tools, Roughing | 9 - 14 | 30 - 45 |
| High-Speed Steel Tools, Finishing | 15 - 18 | 50 - 60 |
| Milling | 6 - 12 | 20 - 40 |
| Reaming - Smooth Finish | 5 - 12 | 15 - 40 |
| Reaming - Work Sizing | 12 - 18 | 40 - 60 |
| High-speed steel reamers. Threading and Tapping | 3 - 8 | 10 - 25 |
| Drilling - High-Speed Drills | 9 - 15 | 30 - 50 |
| ST | Smooth turned | PR | Peeled and reeled |
|---|---|---|---|
| CF | Cold finished | HRAP | Hot rolled annealed and pickled |
| CD | Cold drawn | P | Polished |
| BD | Bright drawn | SRE | Slit rolled edge |
| CG | Centreless ground | HF | Hot finished |
| P&T | Peeled and turned | RT | Rough turned/peeled |
Dependable Nitronic 50 Round Bar Stockist in India backed by a legacy of quality and consistent performance.
| Temperature, °C (°F) | Thermal Conductivity*, W/m·K (BTU/hr·ft·in./°F) |
|---|---|
| 21 (70) | - |
| 149 (300) | 15.6 (108) |
| 316 (600) | 17.9 (124) |
| 482 (900) | 20.3 (141) |
| 649 (1200) | 23.0 (160) |
| 816 (1500) | 25.2 (175) |
| Condition | UTS – Smooth, MPa (ksi) | UTS – Notched, MPa (ksi) |
|---|---|---|
| Annealed 1121 °C (2050 °F) | 790 (114.5) | 1069 (155) |
| Annealed 1066 °C (1950 °F) | 830 (120.5) | – |
| High-Strength (HS) bars | 1041 (151.0) | 1355 (196.5) |
| Property | Value |
|---|---|
| Density (g/cm³) | 8.03 |
| Melting Point (°C) | 1370 – 1390 |
| Electrical Resistivity (µΩ·cm) | 0.75 |
| Coefficient of Thermal Expansion (x10⁻⁶ /°C) | 13.5 |
| Thermal Conductivity (W/m·K) | 15.3 |
| Specific Heat (J/kg·K) | 500 |
Your strategic Nitronic 50 Round Bar Stockist in India for reliable delivery and unmatched material strength.
| Temperature, °C (°F) | Young’s Modulus in Tension | Poisson’s Ratio | |
|---|---|---|---|
| GPa | Mpsi | ||
| 22 (72) | 199 | 28.9 | 0.312 |
| 93 (200) | 192 | 27.8 | 0.307 |
| 149 (300) | 186 | 27.0 | 0.303 |
| 204 (400) | 180 | 26.1 | 0.299 |
| 260 (500) | 174 | 25.3 | 0.295 |
| 315 (600) | 170 | 24.6 | 0.291 |
| 371 (700) | 165 | 24.0 | 0.288 |
| UNS | S20910 |
|---|---|
| International Specifications | Euronorm: XM-19 Werstoff# 1.3964 |
| Specifications | AMS 5764, ASME SB479, ASTM A193 GR.B8R, ASTM A194, ASTM A276 GR. XM-19, ASTM A479 GR. XM-19 |
Certified Nitronic 50 Round Bar Manufacturer in India of high-integrity products with proven resistance to fatigue.
| Condition | UTS, MPa (ksi) | Double Shear, MPa (ksi) | Shear/Tensile Ratio, % |
|---|---|---|---|
| Annealed 1066 °C (1950 °F) | 869 (126) | 598 (86.8) | 69 |
| Annealed 1121 °C (2050 °F) | 779 (113) | 541 (78.5) | 69.5 |
| Temperature, °C (°F)C | Contraction, (ppm) | Mean Expansion Coefficient Between T and 24 °C (75 °F) | |
|---|---|---|---|
| ppm/°F | ppm/°C | ||
| -51 (-60) | 1074 | 7.95 | 14.34 |
| -143 (-225) | 2231 | 7.44 | 13.37 |
| -129 (-200) | 2079 | 7.56 | 13.60 |
| -62 (-80) | 1237 | 7.98 | 14.40 |
| -117 (-178) | 1951 | 7.71 | 13.84 |
| -41 (-41) | 948 | 8.17 | 14.61 |
| -46 (-51) | 1016 | 8.06 | 14.53 |
| -162 (-260) | 2333 | 6.96 | 12.55 |
| -196 (-320) | 2542 | 6.44 | 11.56 |
| -101 (-150) | 1723 | 7.66 | 13.80 |
| -73 (-100) | 1398 | 7.99 | 14.43 |
| -87 (-125) | 1560 | 7.80 | 14.07 |
| Category | Countries | Delivery Time | |
|---|---|---|---|
| Fast Delivery (Under 10 Days) | Singapore |  |
8 Days |
| Kuwait |  |
10 Days | |
| Medium Delivery (25-30 Days) | Germany |  |
20 Days |
| Nigeria |  |
30 Days | |
| Long Delivery (40+ Days) | Libya |  |
45 to 60 Days |
Share your required size and quantity for AWS 165 Threaded Bar; we quote within 24 hours.
ISO 15156-3 Cold Rolled Round Bar is available in mill, pickled, polished or bright finish as per your project.
We source N-50 Stainless Forged Bar from Indian, European and Japanese mills, all fully certified.
Nitronic Alloy 50 Annealed Round Bar is supplied in PH, H&T, ANN condition, or as specified.
There is no fixed MOQ for XM 19 Polished Bar; we supply any quantity.